316 / 316L vlekvrye staal spoel
| Spesifikasies | ASTM A240, ASME SA240 |
| Standaard | JIS, ASTM, AISI, GB, EN, DIN |
| Oppervlak | 2B, BA, HL, nr. 4, spieël ens. |
| Klaar | Koud gerol, Warm gerol |
| Dikte | 0,3 mm – 100 mm |
| Grootte | 1000mm, 1219mm, 1250mm, 1500mm, 1524mm, 2000mm |
Graadspesifikasies vir vlekvrye staal 316 / 316L-rolle
| STANDAARD | WERKSTOF Nr | UNS | JIS | BS | GOST | AFNOR | EN |
| SS 316 | 1.4401 / 1.4436 | S31600 | SUS 316 | 316S31 / 316S33 | - | Z7CND17‐11‐02 | X5CrNiMo17-12-2 / X3CrNiMo17-13-3 |
| SS 316L | 1.4404 / 1.4435 | S31603 | SUS 316L | 316S11 / 316S13 | 03Ch17N14M3 / 03Ch17N14M2 | Z3CND17‐11‐02 / Z3CND18‐14‐03 | X2CrNiMo17-12-2 / X2CrNiMo18-14-3 |
Chemiese eienskappe van SS 316 / 316L spoele
| Graad | C | Mn | Si | P | S | Cr | Mo | Ni | Fe |
| SS 316 | 0,08 maks | 2,0 maks | 1,0 maks | 0,045 maks | 0,030 maks | 16.00 - 18.00 | 2.00 - 3.00 | 11.00 - 14.00 | 67.845 min |
| SS 316L | 0,035 maks | 2,0 maks | 1,0 maks | 0,045 maks | 0,030 maks | 16.00 - 18.00 | 2.00 - 3.00 | 10.00 - 14.00 | 68.89 min |
Meganiese eienskappe van SS 316 / 316L spoele
| Digtheid | Smeltpunt | Trek sterkte | Opbrengssterkte (0,2% verrekening) | Verlenging |
| 8,0 g / cm3 | 1400 ° C (2550 ° F) | Psi - 75000, MPa - 515 | Psi - 30000, MPa - 205 | 35 % |
| 8,0 g / cm3 | 1399 ° C (2550 ° F) | Psi - 75000, MPa - 515 | Psi - 30000, MPa - 205 | 35 % |